Material Name: T8Mn
Standard: GB / T 1298-1986
T8MN Overview
Features and Scope
Performance and use with T8 and T8A similar, good hardenability, the larger cross-section can be used in the manufacture of tools. ● Delivery status: the status of delivery of steel to annealing. By mutual agreement, may not annealed state delivery.
Chemical composition:
Carbon C: 0.80 ~ 0.90
Si Si: ≤ 0.35
Manganese Mn: 0.40 ~ 0.60
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.035
Chromium Cr: allow the residual content of ≤ 0.25, ≤ 0.10 (when manufacturing lead bath quench wire)
Ni: to allow the residual content of ≤ 0.20, ≤ 0.12 (when manufacturing lead bath quench wire)
Copper Cu: to allow the residual content of ≤ 0.30, ≤ 0.20 (when manufacturing lead bath quench wire)
Note: The allows the residual content of Cr + Ni + Cu ≤ 0.40 (when manufacturing lead-bath hardening steel) [2]
- Phone:021-57866678
021-57866679
Fax: 021-57860199
Cont:Mr.Huang 13818168036
Mr.Zhao 13919185505
Email: shzlgt99@163.com
Website:www.shzlgt99.com
Address:Shanghai fengxian, taikang town highway number 118