60Si2CrA spring steel, compared with Si-Mn steel, while plastic similar, with high tensile strength and yield strength, greater hardenability of steel, have temper brittleness. 60Si2CrA to withstand high stress and temperature at 300 ~ 350 ℃ the following spring, such as the governor springs, turbine steam seal springs, disc springs high-pressure water pump, condenser bearing springs and other spring breakers to use.
Chemical composition
Carbon C: 0.56 ~ 0.64
Si Si: 1.40 ~ 1.80
Manganese Mn: 0.40 ~ 0.70
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.030
Chromium Cr: 0.70 ~ 1.00
Ni-Ni: ≤ 0.35
Copper Cu: ≤ 0.25
Mechanical properties
Tensile strength σb (MPa): ≥ 1764 (180)
Yield strength σs (MPa): ≥ 1568 (160)
Elongation δ5 (%): ≥ 6
Reduction of area ψ (%): ≥ 20
Hardness: hot-rolled + heat treatment, ≤ 321HB; cold-drawn + heat treatment, ≤ 321HB
Standard heat treatment and microstructure
Standard heat treatment: quenching 870 ℃ ± 20 ℃, oil cooling; tempering 420 ℃ ± 50 ℃ (special needs, ± 30 ℃).
60si2cra density ρ = 7.81 g / cc, the steel can be cold rolled into plate, strip and wire, making the spring. 60si2cra can also be made into such fitter's chisel, stylus and other tools. 60si2cra can be made of steel section size is generally about 8 ~ 15mm small springs such as various small flat, round springs, bottom spring pads, spring winding.
- Phone:021-57866678
021-57866679
Fax: 021-57860199
Cont:Mr.Huang 13818168036
Mr.Zhao 13919185505
Email: shzlgt99@163.com
Website:www.shzlgt99.com
Address:Shanghai fengxian, taikang town highway number 118
60si2crA
Public Time:2011年05月14日 | Sort:Spring steel | Hits:1004