Germany X153Crmov12
Public Time:2011年05月14日 | Sort:Alloy steel | Hits:1033

Details:
Material Name: Alloy tool steel
Grade: X153Crmov12
Standard: GB / T 1299-1985
Features and application:
Composition, performance and 5CrW2Si similar single higher quenching hardness and high temperature strength. Often used as wear resistance to withstand high impact loads but requires tools such as pneumatic tools, chisels and heavy-duty work performance molds, cold shear blades, pneumatic hammers and other tools.
Chemical Composition:
Carbon C: 0.55 ~ 0.65
Si Si: 0.50 ~ 0.80
Manganese Mn: ≤ 0.40
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.030
Chromium Cr: 1.00 ~ 1.30
Ni: to allow the residual content of ≤ 0.25
Copper Cu: to allow the residual content of ≤ 0.30
Tungsten W: 2.00 ~ 2.70
Mechanical Properties:
Hardness: Annealed, 285 ~ 229HB, indentation diameter of 3.6 ~ 4.0mm; quenching, ≥ 57HRC
Heat treatment and microstructure specifications:
Heat treatment specifications: sample chemical composition:

Alloy
Trademark
     Fe Fe Ni-Cr-Mo Mo <> Tungsten W Co C Co C Mn Si Si Mn P S S P> V titanium vanadium
Ti quenching 860 ~ 900 ℃, oil cooling.
Delivery status: ● Features and steel to the scope of application:
Cold work die steel, is the introduction of the U.S. steel A2, Class A space in the quenched steel is the most widely used one. Applies to both wear and toughness of cold work die steel requirements, can replace CrWMn, 9Mn2V steel production, small cold stamping die, die cutting, molding and red top.
Chemical Composition:
Carbon C: 0.95 ~ 1.05
Si Si: ≤ 0.50
Manganese Mn: ≤ 1.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.030
Chromium Cr: 4.75 ~ 5.50
Ni: to allow the residual content of ≤ 0.25
Copper Cu: to allow the residual content of ≤ 0.30
Vanadium V: 0.15 ~ 0.50
Mo Mo: 0.90 ~ 1.40
Mechanical Properties:
Hardness: Annealed, ≤ 255HB, indentation diameter ≥ 3.95mm; quenching, ≥ 60HRC
Heat treatment and microstructure specifications:
Standard heat treatment: quenching, 790 ± 15 ℃ warm-up, 940 ± 6 ℃ (salt) or 950 ± 6 ℃ (controlled atmosphere furnace) heating, insulation 5 ~ 15min, air-cooled, 200 ± 6 ℃ tempering.
Delivery status: the status of delivery of steel to annealing. Annealed state delivery.