Details:
● Chemical Composition:
Carbon C: 0.37 ~ 0.45 (promise deviation: ± 0.01)
Si Si: ≤ 0.20
Manganese Mn: 0.30 ~ 0.60 (promise deviation: ± 0.02)
Sulfur S: ≤ 0.035
Phosphorus P: ≤ 0.035
Chromium Cr: promised to the residual content of ≤ 0.020
Ni: to promise the residual content of ≤ 0.020
Copper Cu: agreed to the residual content of ≤ 0.020
● Mechanical Properties: Tensile strength σb (MPa): ≥ 569 (58) yield strength σs (MPa): ≥ 333 (34) Elongation δ5 (%): ≥ 19 Reduction of area ψ (%): ≥ 45 Hardness : (hot) ≤ 217HB, indentation diameter ≥ 4.1mm; (annealing) ≤ 187HB, indentation diameter ≥ 4.4mm
● Heat treatment and microstructure specifications: standard heat treatment: heating to the critical point than the AC3 30 ~ 50 ℃ high temperature, holding time less than 30min, air-cooled.
● Delivery status: in Hot state of delivery. The agreement can also be delivered by the annealed condition.
- Phone:021-57866678
021-57866679
Fax: 021-57860199
Cont:Mr.Huang 13818168036
Mr.Zhao 13919185505
Email: shzlgt99@163.com
Website:www.shzlgt99.com
Address:Shanghai fengxian, taikang town highway number 118
Japan SWRCH40K
Public Time:2011年05月14日 | Sort:Alloy steel | Hits:1010