Made of stainless steel
Position:Home >> Products >> Made of stainless steel
4Cr13
Public Time:2011年05月13日 | Sort:Made of stainless steel | Hits:1443

Standard: GB / T 1220-1992
4cr13 Introduction
Features and application:
  3Cr13 4Cr13 features high hardness after quenching than some corrosion resistance. Use for cutting, nozzle, valve seats and so on. 1Cr17Ni2 features strong resistance to nitric acid and organic acid corrosion. Use as a high hardness and high wear resistance of heat pumps, valves, valve bearings, medical equipment, spring and other parts.

 

Chemical composition
Chemical Composition:
  Carbon C: 0.36 ~ 0.48
  Si Si: ≤ 0.60
  Manganese Mn: ≤ 0.80
  Sulfur S: ≤ 0.030
  Phosphorus P: ≤ 0.035
  Chromium Cr: 12.00 ~ 14.00
  Ni: to allow containing ≤ 0.60

 

Mechanical properties
Mechanical Properties:
  Hardness: Annealed,, ≤ 201HB, indentation diameter of 3.9 ~ 4.3mm; quenching, ≥ 50HV
Heat treatment and microstructure specifications:
  Heat treatment specifications: 1) annealing, 800 ~ 900 ℃ slow cooling or rapid cooling of about 750 ℃​​; 2) quenching, 1050 ~ 1100 ℃ oil cooling; 3) temper, 200 ~ 300 ℃ fast-cooling.
Microstructure: Organizing for the martensitic type.

 

Delivery status
Delivery status: the status of delivery of steel to annealing. Blacksmithing: oil quenching cold cracking susceptibility of some tool steel, forging heating should not be rapidly heated, preferably 650-750 degrees for a warm-up, forging heating temperature of 1130-1150 degrees, the final forging temperature should be greater than 800 - 850 degrees, take the upper ingot forging temperature. Lower temperature when you get the blank forging

 

Annealing
Annealing generally used 780-800 degrees, heat 4-6 hours to ≤ 50 degrees / hour, cooled to 550 degrees baked cooled, isothermal annealing using 700-800 degree heat 2-4 sales, then 670-720 degree heat, to maintain 2-4 hours to ≤ 50 ° / hr cooling rate, cooling to 500 degrees baked cooled, annealed hardness of 241-197HB

 

Heat treatment
And heat treatment on the curve shown in Figure 4-17-1 and Figure 4-17-2, and heat treatment on the performance table shown in Table 4-17-9 and 4-17-10. Good oxidation resistance of the steel can be 600 ~ 650 ℃ long-term use.