SUS305 stainless steel, strong corrosion resistance alloys, work hardening rate for deep stamping and spinning shape.
SUS305 (18Cr-12Ni-0.1C), compared with 304, work hardening is low. For spinning forming, special drawing and cold rolling and so on. SUS305 stainless steel
1, Summary:
        Austenitic stainless steel. And 304 comparison, the high nickel. Welding position bending, and other excellent functional.
2, features:
        1) The welding of the good;
        2) The bending performance is good;
        3) After hardening occurred after heat treatment;
        4) non-magnetic;
3 Scope of application - chemical containers, machinery and equipment parts, heat parts of the equipment, cryogenic components.
4, SUS305 chemical composition (JIS G 4305-2005) (wt%) C Si Mn Cr PS Ni ≤ 0.12 ≤ 1.0 ≤ 2.0 17 ~ 19 ≤ 0.045 ≤ 0.030 10.5 ~ 13.0
5, SUS305 mechanical properties of YS (MPa) TS (MPa) EL Hv ≥ 175 ≥ 480 ≥ 40 ≤ 200
6, using state solution annealed state: NO.1, 2D, 2B, etc.
7, SUS305 application: SUS305 increased more than 304 nickel content, timeliness, and deep-drawing performance is more superior than the 304, can be widely used in various applications.