0Cr19Ni13Mo3 stainless steel
● Features and application:
0Cr19Ni13Mo3 stainless steel corrosion resistant than 0Cr17Ni2Mo2 good points, such as dyeing equipment and materials.
● Chemical Composition:
Carbon C: ≤ 0.08
Si Si: ≤ 1.00
Manganese Mn: ≤ 2.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.035
Chromium Cr: 18.00 ~ 20.00
Ni-Ni: 11.00 ~ 15.00
Mo Mo: 3.00 ~ 4.00
● Mechanical Properties:
Tensile strength σb (MPa): ≥ 520
Conditions yield strength σ0.2 (MPa): ≥ 205
Elongation δ5 (%): ≥ 40
Reduction of area ψ (%): ≥ 60
Hardness: ≤ 187HB; ≤ 90HRB; ≤ 200HV
● Heat treatment and microstructure specifications:
Standard heat treatment: solution 1010 ~ 1150 ℃ fast-cooling. Microstructure: Organizing for the austenitic type.
● Delivery status: normal to heat treatment delivery, the treatment types specified in the contract; not indicated, according to the heat treatment state of delivery.
● Features and application:
0Cr19Ni13Mo3 stainless steel corrosion resistant than 0Cr17Ni2Mo2 good points, such as dyeing equipment and materials.
● Chemical Composition:
Carbon C: ≤ 0.08
Si Si: ≤ 1.00
Manganese Mn: ≤ 2.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.035
Chromium Cr: 18.00 ~ 20.00
Ni-Ni: 11.00 ~ 15.00
Mo Mo: 3.00 ~ 4.00
● Mechanical Properties:
Tensile strength σb (MPa): ≥ 520
Conditions yield strength σ0.2 (MPa): ≥ 205
Elongation δ5 (%): ≥ 40
Reduction of area ψ (%): ≥ 60
Hardness: ≤ 187HB; ≤ 90HRB; ≤ 200HV
● Heat treatment and microstructure specifications:
Standard heat treatment: solution 1010 ~ 1150 ℃ fast-cooling. Microstructure: Organizing for the austenitic type.
● Delivery status: normal to heat treatment delivery, the treatment types specified in the contract; not indicated, according to the heat treatment state of delivery.