Details:
Grade: 00Cr19Ni10NbN
● Features and application: to eliminate intergranular corrosion Application: Suitable for manufacturing requires a certain strength of structural parts.
● Chemical Composition: C: ≤ 0.08 Si Si: ≤ 1.00 Mn Mn: ≤ 2.00 Sulfur S: ≤ 0.030 P P: ≤ 0.035 Chromium Cr: 18.00 ~ 20.00 Nickel Ni: 7.50 ~ 10.50 Niobium Nb: ≤ 0.15 N N: 0.15 ~ 0.30
● Mechanical Properties: Tensile strength σb (MPa): ≥ 685 conditions, yield strength σ0.2 (MPa): ≥ 345 Elongation δ5 (%): ≥ 35 Reduction of area ψ (%): ≥ 50 Hardness: ≤ 250HB ; ≤ 100HRB; ≤ 260HV
● Heat treatment and microstructure specifications: standard heat treatment: solution 1010 ~ 1150 ℃ fast-cooling. Microstructure: Organizing for the austenitic type.
● Delivery status: normal to heat treatment delivery, the treatment types specified in the contract; not indicated, according to the heat treatment state of delivery.
Grade: 00Cr19Ni10NbN
● Features and application: to eliminate intergranular corrosion Application: Suitable for manufacturing requires a certain strength of structural parts.
● Chemical Composition: C: ≤ 0.08 Si Si: ≤ 1.00 Mn Mn: ≤ 2.00 Sulfur S: ≤ 0.030 P P: ≤ 0.035 Chromium Cr: 18.00 ~ 20.00 Nickel Ni: 7.50 ~ 10.50 Niobium Nb: ≤ 0.15 N N: 0.15 ~ 0.30
● Mechanical Properties: Tensile strength σb (MPa): ≥ 685 conditions, yield strength σ0.2 (MPa): ≥ 345 Elongation δ5 (%): ≥ 35 Reduction of area ψ (%): ≥ 50 Hardness: ≤ 250HB ; ≤ 100HRB; ≤ 260HV
● Heat treatment and microstructure specifications: standard heat treatment: solution 1010 ~ 1150 ℃ fast-cooling. Microstructure: Organizing for the austenitic type.
● Delivery status: normal to heat treatment delivery, the treatment types specified in the contract; not indicated, according to the heat treatment state of delivery.