SUS316N stainless steel, corresponding to the national standard 0Cr17Ni12Mo2N, American Standard 316N/S31651. SUS316N is adding 316 N, in the inhibition of extended performance while improving strength, have the effect of reducing the material thickness. Is an excellent corrosion resistance of high strength materials. SUS316N stainless steel
Chemical composition:
Carbon C ≤ 0.08
Si Si ≤ 1.00
Manganese Mn ≤ 2.00
Sulfur S ≤ 0.030
P P ≤ 0.035
Chromium Cr 16.00 ~ 18.00
Ni-Ni: 10.00 ~ 14.00
Mo Mo: 2.00 ~ 3.00
N N: 0.10 ~ 0.22
Mechanical properties:
Tensile strength σb (MPa) ≥ 550
Conditions yield strength σ0.2 (MPa) ≥ 275
Elongation δ5 (%) ≥ 35
Reduction of area ψ (%) ≥ 50
Hardness: ≤ 217HB; ≤ 95HRB; ≤ 220HV
Chemical composition:
Carbon C ≤ 0.08
Si Si ≤ 1.00
Manganese Mn ≤ 2.00
Sulfur S ≤ 0.030
P P ≤ 0.035
Chromium Cr 16.00 ~ 18.00
Ni-Ni: 10.00 ~ 14.00
Mo Mo: 2.00 ~ 3.00
N N: 0.10 ~ 0.22
Mechanical properties:
Tensile strength σb (MPa) ≥ 550
Conditions yield strength σ0.2 (MPa) ≥ 275
Elongation δ5 (%) ≥ 35
Reduction of area ψ (%) ≥ 50
Hardness: ≤ 217HB; ≤ 95HRB; ≤ 220HV