Stainless steel 0Cr18Ni16Mo5
Grade: 0Cr18Ni16Mo5
Standard: GB / T 1220-1992
● Features and application:
Absorb chlorine ion solution used in the manufacture of heat exchangers, equipment acetic acid, phosphoric acid equipment, bleaching devices, and 00Cr17Ni13Mo3 00Cr17Ni14Mo2 not apply in the environment.
● Chemical Composition:
Carbon C: ≤ 0.040
Si Si: ≤ 1.00
Manganese Mn: ≤ 2.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.035
Chromium Cr: 16.00 ~ 19.00
Ni-Ni: 15.00 ~ 17.00
Mo Mo: 4.00 ~ 6.00
● Mechanical Properties:
Tensile strength σb (MPa): ≥ 480
Conditions yield strength σ0.2 (MPa): ≥ 177
Elongation δ5 (%): ≥ 40
Reduction of area ψ (%): ≥ 45
Hardness: ≤ 187HB; ≤ 90HRB; ≤ 200HV
● Heat treatment and microstructure specifications:
Standard heat treatment: solution 1030 ~ 1180 ℃ fast-cooling
Microstructure: Organizing for the austenitic
● Delivery status: normal to heat treatment delivery, the treatment types specified in the contract; not indicated, according to the non-heat treatment delivery
Grade: 0Cr18Ni16Mo5
Standard: GB / T 1220-1992
● Features and application:
Absorb chlorine ion solution used in the manufacture of heat exchangers, equipment acetic acid, phosphoric acid equipment, bleaching devices, and 00Cr17Ni13Mo3 00Cr17Ni14Mo2 not apply in the environment.
● Chemical Composition:
Carbon C: ≤ 0.040
Si Si: ≤ 1.00
Manganese Mn: ≤ 2.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.035
Chromium Cr: 16.00 ~ 19.00
Ni-Ni: 15.00 ~ 17.00
Mo Mo: 4.00 ~ 6.00
● Mechanical Properties:
Tensile strength σb (MPa): ≥ 480
Conditions yield strength σ0.2 (MPa): ≥ 177
Elongation δ5 (%): ≥ 40
Reduction of area ψ (%): ≥ 45
Hardness: ≤ 187HB; ≤ 90HRB; ≤ 200HV
● Heat treatment and microstructure specifications:
Standard heat treatment: solution 1030 ~ 1180 ℃ fast-cooling
Microstructure: Organizing for the austenitic
● Delivery status: normal to heat treatment delivery, the treatment types specified in the contract; not indicated, according to the non-heat treatment delivery