Stainless steel 00Cr17Ni13Mo2N
Material Name: Stainless steel rod
Grade: 00Cr17Ni13Mo2N
Standard: GB / T 1220-1992
● Features and application:
Add 00Cr17Ni14Mo2 in Grade N, has the same properties, uses and 0Cr17Ni12Mo2N the same, but better resistance to intergranular corrosion.
● Chemical Composition:
Carbon C: ≤ 0.030
Si Si: ≤ 1.00
Manganese Mn: ≤ 2.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.035
Chromium Cr: 16.00 ~ 18.50
Ni-Ni: 10.50 ~ 14.50
Mo Mo: 2.00 ~ 3.00
N N: 0.12 ~ 0.22
● Mechanical Properties:
Tensile strength σb (MPa): ≥ 550
Conditions yield strength σ0.2 (MPa): ≥ 245
Elongation δ5 (%): ≥ 40
Reduction of area ψ (%): ≥ 50
Hardness: ≤ 217HB; ≤ 95HRB; ≤ 220HV
● Heat treatment and microstructure specifications:
Standard heat treatment: solution 1010 ~ 1150 ℃ fast-cooling.
Microstructure: Organizing for the austenitic type.
Material Name: Stainless steel rod
Grade: 00Cr17Ni13Mo2N
Standard: GB / T 1220-1992
● Features and application:
Add 00Cr17Ni14Mo2 in Grade N, has the same properties, uses and 0Cr17Ni12Mo2N the same, but better resistance to intergranular corrosion.
● Chemical Composition:
Carbon C: ≤ 0.030
Si Si: ≤ 1.00
Manganese Mn: ≤ 2.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.035
Chromium Cr: 16.00 ~ 18.50
Ni-Ni: 10.50 ~ 14.50
Mo Mo: 2.00 ~ 3.00
N N: 0.12 ~ 0.22
● Mechanical Properties:
Tensile strength σb (MPa): ≥ 550
Conditions yield strength σ0.2 (MPa): ≥ 245
Elongation δ5 (%): ≥ 40
Reduction of area ψ (%): ≥ 50
Hardness: ≤ 217HB; ≤ 95HRB; ≤ 220HV
● Heat treatment and microstructure specifications:
Standard heat treatment: solution 1010 ~ 1150 ℃ fast-cooling.
Microstructure: Organizing for the austenitic type.