316Ti stainless steel grades is the Chinese national standard 0Cr18Ni12Mo2Ti 1Cr18Ni12Mo2Ti stainless steel plate, 316Ti stainless steel plate is added to Ti in the SUS316 steel to improve resistance to intergranular corrosion. Used to resist sulfuric acid, phosphoric acid, acetic acid, acetic acid equipment.
Chemical composition:
C: ≤ 0.08
Si ≤ 1.00
Mn ≤ 2.00
P ≤ 0.035
S ≤ 0.030
Ni 11.00 ~ 14.00
Cr 16.00 ~ 19.00
Mo 1.80 ~ 2.50
Ti ≥ 5 * C% ~ 0.70
GB/T1220-1992 have this requirement and are usually called Mo2Ti or 316Ti
Mechanical properties:
YS (Mpa) ≥ 205
TS (Mpa) ≥ 520
EL (%) ≥ 40
Hv 200 ° around
Thickness: 2B cold rolled plate (0.09-6.0mm); hot-rolled industrial sheet No.1 (3-50mm) plate, chemical sheet, hot plate;
Width: 5mm --- 850mm steel; 1000,1219,1250,1500,1800,2000 mm coil, flat
Surface: 2B smooth, No.1 industrial area, BA (6k) Mirror, 8K mirror, 9K mirror, brushed surface, matte surface.
Origin: domestic and imported (Sweden, Japan, Finland, South Korea, South Africa, Taiwan);
Chemical composition:
C: ≤ 0.08
Si ≤ 1.00
Mn ≤ 2.00
P ≤ 0.035
S ≤ 0.030
Ni 11.00 ~ 14.00
Cr 16.00 ~ 19.00
Mo 1.80 ~ 2.50
Ti ≥ 5 * C% ~ 0.70
GB/T1220-1992 have this requirement and are usually called Mo2Ti or 316Ti
Mechanical properties:
YS (Mpa) ≥ 205
TS (Mpa) ≥ 520
EL (%) ≥ 40
Hv 200 ° around
Thickness: 2B cold rolled plate (0.09-6.0mm); hot-rolled industrial sheet No.1 (3-50mm) plate, chemical sheet, hot plate;
Width: 5mm --- 850mm steel; 1000,1219,1250,1500,1800,2000 mm coil, flat
Surface: 2B smooth, No.1 industrial area, BA (6k) Mirror, 8K mirror, 9K mirror, brushed surface, matte surface.
Origin: domestic and imported (Sweden, Japan, Finland, South Korea, South Africa, Taiwan);