60CrMnA spring steel
Material Name: 60CrMnA spring steel
Standard: GB / T 1222-1984
Features and Scope
60CrMnA spring steel high strength, ductility and toughness, good hardenability, heat-sensitive than the low-manganese steel, higher than the Si-Mn steel, silico-manganese steel decarburization tendency than the small, temper brittleness. 60CrMnA for vehicles, tractors and industrial production of heavy load, stress and a larger spring diameter larger coil spring.
Chemical composition
Carbon C: 0.56 ~ 0.64 Si Si: 0.17 ~ 0.37
Manganese Mn: 0.70 ~ 1.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.030
Chromium Cr: 0.70 ~ 1.00
Ni-Ni: ≤ 0.35
Copper Cu: ≤ 0.25
Mechanical properties
Tensile strength σb (MPa): ≥ 1225 (125)
Conditions yield strength σ0.2 (MPa): ≥ 1078 (110)
Elongation δ5 (%): ≥ 9 (for reference)
Reduction of area ψ (%): ≥ 20
Hardness: hot, ≤ 321HB; cold-drawn + heat treatment, ≤ 321HB
Material Name: 60CrMnA spring steel
Standard: GB / T 1222-1984
Features and Scope
60CrMnA spring steel high strength, ductility and toughness, good hardenability, heat-sensitive than the low-manganese steel, higher than the Si-Mn steel, silico-manganese steel decarburization tendency than the small, temper brittleness. 60CrMnA for vehicles, tractors and industrial production of heavy load, stress and a larger spring diameter larger coil spring.
Chemical composition
Carbon C: 0.56 ~ 0.64 Si Si: 0.17 ~ 0.37
Manganese Mn: 0.70 ~ 1.00
Sulfur S: ≤ 0.030
Phosphorus P: ≤ 0.030
Chromium Cr: 0.70 ~ 1.00
Ni-Ni: ≤ 0.35
Copper Cu: ≤ 0.25
Mechanical properties
Tensile strength σb (MPa): ≥ 1225 (125)
Conditions yield strength σ0.2 (MPa): ≥ 1078 (110)
Elongation δ5 (%): ≥ 9 (for reference)
Reduction of area ψ (%): ≥ 20
Hardness: hot, ≤ 321HB; cold-drawn + heat treatment, ≤ 321HB