SK5 carbon tool steel
SK85 (SK5)
Carbon tool steel
Standard: JIS G4401 ● Features and application: after quenching and tempering high hardness and wear resistance, but low thermal rigid, hardenability is poor, deformation, ductility and lower strength. As a need to have a high hardness and wear resistance of tools, such as the shape of a simple mold and punch, metal cutting tools, drilling tools, woodworking cutters, hard drilling, axes, chisels, hand saws vertical , and the fitter assembly tools, dies and other secondary rivet tool.
● Chemical Composition: C: 0.80 ~ 0.90 Si Si :0.10-0 .35 Mn Mn :0.10-0 .50 S S: ≤ 0.030 P P: ≤ 0.030 Chromium Cr: allow the residual content of ≤ 0.25, ≤ 0.10 (when manufacturing lead-bath quenching wire ) Ni: to allow the residual content of ≤ 0.20, ≤ 0.12 (when manufacturing lead bath quench wire) copper Cu: to allow the residual content of ≤ 0.30, ≤ 0.20 (when manufacturing lead-bath hardening steel) Note: The allows the residual content of Cr + Ni + Cu ≤ 0.40 (when manufacturing lead bath quench wire)
● Mechanical Properties: Hardness: Annealed, ≤ 187HB, indentation diameter ≥ 4.40mm; quenching, ≥ 62HRC
● Heat treatment and microstructure specifications: standard heat treatment: quenching the sample 780 ~ 820 ℃, water-cooled.
● Delivery status: the status of delivery of steel to annealing. By mutual agreement, may not annealed state delivery.
- Phone:021-57866678
021-57866679
Fax: 021-57860199
Cont:Mr.Huang 13818168036
Mr.Zhao 13919185505
Email: shzlgt99@163.com
Website:www.shzlgt99.com
Address:Shanghai fengxian, taikang town highway number 118